Titanium Sheet
Category:Non-ferrous metals
Color:Matt color
Luster:Metallic luster
Transparency：Opaque
Hardness：HB150-HB340
Specific gravity:4.51
Application：Aviation, chemical, petroleum, machinery, medical and other industries
titanium sheet
There are two standards for titanium plate. The national standard is GB/T3621-2007 and GB/T13810-2007, and the American standard is ASTM B265, ASTM F136, ASTM F67, and AMS4928.
brand
American brand: GR1, GR2, GR3, GR5, GR7, GR12
Russian brand: BT1-00, BT1-0, BT1-2, etc.
Domestic brand: TA0, TA2, TA3, TA5, TA6, TA7, TA9, TA10, TB2, TC1, TC2, TC3, TC4
Reference standard
1: GB 228 Metal tensile test method
2: GB/T 3620.1 Titanium and titanium alloy brand and chemical composition
3: GB/T3620.2 Titanium and titanium alloy processing products chemical composition and composition tolerance
4: GB 4698 Sponge titanium, titanium and ferroalloy chemical analysis method
Titanium plate specifications
Grade： TA1, TA2, TA3, TC4, GR1, GR2, GR5
Standard ：GB/T 3621-2007, GB/T 13810-2007ASTM B265, ASTM F136, ASTM F67,
Size ：T 0.5-5.0mm x W1000mm x L 2000-3500mmT 6.0- 30mm x W1000-2500mm x L 3000-6000mmT 30- 80mm x W1000mm x L 2000mm
Application ：Metallurgy, electronics, medical treatment, chemical industry, petroleum, medicine, aerospace, etc.
Titanium plate thickness tolerance
| thickness(mm) | Thickness tolerance(mm) |
| (3.71 to 4.76), excl | 0.36 |
| 3.33 to 3.68 | 0.31 |
| 2.92 to 3.30 | 0.25 |
| 2.51 to 2.90 | 0.23 |
| 2.13 to 2.49 | 0.20 |
| 1.85 to 2.11 | 0.18 |
| 1.50 to 1.83 | 0.15 |
| 1.04 to 1.47 | 0.13 |
| 0.69 to 1.02 | 0.10 |
| 0.43 to 0.66 | 0.08 |
| 0.20 to 0.41 | 0.05 |
| 0.15 to 0.18 | 0.04 |
| 0.13 | 0.03 |
Titanium plate manufacturing process
Hot forging is a forging process performed above the metal recrystallization temperature.
Hot rolling is a rolling process performed above the recrystallization temperature.
Cold rolling is a rolling process in which the plastic deformation temperature is lower than the recovery temperature.
Annealing: A metal heat treatment process in which the metal is slowly heated to a certain temperature, kept for a sufficient time, and then cooled at an appropriate speed (usually slowly cooled, sometimes controlled cooling).
Pickling: Immersing the workpiece in an aqueous solution of sulfuric acid to remove oxides and other films on the metal surface. It is a pretreatment or intermediate treatment for processes such as electroplating, enamelling, and rolling.
Characteristics of titanium plate
1. The surface oxide film of the titanium seed plate is equivalent to a good, durable and wear-resistant separator. The use of titanium seed plates saves separators, makes it easy to peel off the plates, and eliminates the process of pre-treatment of the seed plates. Titanium seed plates are half lighter than copper seed plates.
2. The service life of titanium seed plate is more than 3 times that of copper seed plate, which can reach 10 to 20 years depending on the operating conditions
3. The electrolytic copper produced by titanium seed plate has dense crystal structure, smooth surface and excellent quality.
4. Since titanium seed plate does not need to be coated with a separator, it can avoid contamination of copper electrolyte.
5. Increasing production capacity reduces the production cost of electrolytic copper, thus achieving better economic benefits.
Hot Tags: titanium sheet, China titanium sheet manufacturers, suppliers, factory, gr2 titanium plate, gr7 titanium sheet, titanium foil, titanium for food industry, titanium for mining, titanium manufacturing
You Might Also Like
Send Inquiry